Atomized iron powder

Application:

in production of powder parts for antifriction, construction and electro technical purposes, sintered electrode tape, frictional disks;
in flux-oxygen cutting of metals, as a basic component of high- production electrodes
in production of printing inks, as a catalyst and reducing agent of different chemical production, in magnetic flaw detection.

Iron powder is produced by means of spraying molten metal by high-pressure water of such grades: ПЖР 3.200.28-30, ПЖР 3.315. 26-28, ПЖР 3.450.28-30.

Technical specifications: ГОСТ 9849-86 "Порошок железный" with modifications №1,2.

Iron powder of grade ПЖР 3.200.28

ПЖР	3	200	28
Atomized iron powder	Chemical composition (tabl.1)	Grain-size category(tabl. 2)	Bulk density(tabl. 3)

Specifications

Table 1. Chemical composition

Grade	Iron	Мass fraction, % not more
Grade	Iron	Carbon	Silicon	Manganese	Sulfur	Phosphorus	Oxygen
ПЖР 3	Base	0.05	0.08	0.20	0.02	0.02	0.5

Table 2. Grain composition

Grain-size category	Fractional yield,% at particle size, mm
Grain-size category	from 0.063 to 0.45	from 0.45 to 0.0315	from 0.0315 to 0.25	from 0.25 to 0.20	from 0.20 to 0.16	from 0.16 to 0.045	less than 0.045
450	0-5	balance				10-30	0-10
315	—	0.10	43952	balance		30-55	0-15
200	—	—	—	0-1.5	0-15	balance	10-15

Table 3. Bulk density

Marking of bulk density	Bulk density g/cm³	Strength of compacts H/mm²	Flowability, s/50g, not more	Compressibility g/cm³ (700 MPa)
26	from 2.5 to 2.7	18	35	6.9
28	from 2.7 to 2.9	14	32
30	more than 2.9	10	30